Investigation into the Effect of Use of Metal Primer on Adhesion of Heat Cure Acrylic Resin to Cast Titanium: An In Vitro Study

Abstract The availability of adhesive primers capable of bonding chemically to base metal alloys without well defined passive oxide surface film has been improved significantly over the last decade. Therefore, the purpose of the study was to compare and evaluate the effect of metal primer on adhesion of heat cure acrylic resin to cast titanium. Shear bond strength test was conducted on 80 commercially pure titanium cast metal heat-cure acrylic resin discs treated with different surface treatments. The first group received no surface treatment (group I); the second group was subjected to sandblasting (group II); the third group was treated with bonding agent (alloy primer) (group III) and the fourth was treated with sandblasting and alloy primer (group IV). After the samples were surface treated, acrylic resin was mixed, packed and processed over the test area of cast titanium. Ten specimens of each group were immersed in distilled water for 24 h followed by thermocycling for 20,000 cycles. Shear bond-strength between the heat cure acrylic resin and titanium was evaluated using Instron universal testing machine. Debonded specimens of all the groups were subjected to SEM analysis. The bond failure (MPa) was analyzed by ANOVA and Duncan’s multiple comparison tests. Surface treatment with sandblasting, followed by the application of alloy primer showed maximum shear bond strength before and after thermocycling (24.50 ± 0.59 and 17.39 ± 1.56 MPa respe...
Source: The Journal of Indian Prosthodontic Society - Category: Orthopaedics Source Type: research