Less Midterm Damage and Oxidation Are Seen in Retrieved Highly Crosslinked Ultrahigh-Molecular-Weight Polyethylene Tibial Inserts than in Direct Compression Molded Polyethylene Inserts

ConclusionsSurface damage and oxidation are reduced in XLPE inserts compared to compPE at midterm follow-up. Peak OI greater than 1.0 in the compPE group suggests that mechanical-property degradation had occurred, a likely cause for increased damage. Longer-term retrievals will determine whether these trends continue. Based on midterm results, XLPE shows an advantage over compression molded PE in total knee arthroplasty.