Effect of SnO, MgO and Ag2O Mix-doping on the Formation and Superconducting Properties of Bi-2223 Ag/tapes

Publication date: 2016 Source:Physics Procedia, Volume 81 Author(s): X.Y. Lu, D. Yi, H. Chen, A. Nagata The Ag/tapes with the composition Bi1.8Pb0.4Sr1.9Ca2.1Cu3.5Oy + x wt% SnO + y wt% MgO + z wt% Ag2O (x = 0, 0.2, 0.4; y = 0, 0.2; z = 0, 0.2) were prepared by sintering at 835°C for 120h after partial-melting at 845°C for 1h. The individual SnO doping, SnO and Ag2O mix-doping, and SnO and MgO mix-doping all decrease the conversion of Bi-2212 phase to Bi-2223 phase. The tape with individual 0.4 wt% SnO doping shows the lowest conversion and the lowest critical current density. However, the SnO, MgO and Ag2O mix-doping increase the conversion of Bi-2212 phase to Bi-2223 phase. The tape with 0.2 wt% SnO, 0.2 wt% MgO and 0.2 wt%Ag2O mix-doping shows the highest proportion of Bi-2223 phase and the highest critical current density.

Source: Physics Procedia - May 9, 2016 Category: Physics Source Type: research